New clean epoxy resin flame retardant - DOPO products come out
Ammonium molybdate is mainly used for smelting ferromolybdenum and preparing molybdenum trioxide and metal Molybdenum Powder; as raw material for tungsten-molybdenum alloy and molybdenum wire; for geological exploration of phosphate rock; for chemical catalyst; a small amount for agricultural molybdenum Fertilizer; a very small amount is used in medicine; as a component of various enzymes, the lack of molybdenum can lead to dental caries, kidney stones, Keshan disease, Kashin-Beck disease, esophageal cancer and other diseases. Ammonium Molybdate,99.5% Ammonium Molybdate For Fertilizer,High Purity Ammonium Molybdate,Ndustrial Ammonium Molybdate Jiangsu Lucky Metal Materials Co., Ltd. , https://www.luckymetalmoly.com
In this respect, research and development are mainly concentrated in two directions: one is to use DOPO derivatives as reactive flame retardants, introduced into the ring resin matrix structure, and then cured to obtain phosphorus-containing epoxy resin; the second is to cure with DOPO derivatives. The agent cures the ordinary epoxy resin to form a phosphorus-containing epoxy resin. In this paper, the new varieties of epoxy resin flame retardants and curing agents used in domestic and foreign DOPO derivatives and the flame retardancy and thermal properties are reviewed. In the development and application of flame retardants, DOPO(I) was reacted with itaconic acid, maleic acid and benzoquinone respectively to obtain three kinds of DOPO derivatives II, III and IV, and I-IV was reacted with epoxy resin to obtain high. Performance epoxy resin, cured product with high Tg, Td and high modulus of elasticity and good flame retardancy, suitable for printed circuit boards and semiconductor packages. U.S. Patent] proposes a new type of flame retardant V, which is formed by the reaction of DOPO with naphthoquinone. This phosphorus-containing epoxy resin exhibits higher curing than tetrabromobisphenol A (TBBA) type cured epoxy resin. Thermal stability and carbonization rate.
In the development of curing agents, DOPO polyphenolic hydroxyl or polyamino derivatives can be used as curing agents for polymers. The properties of epoxy resins cured by them are quite different from those of brominated epoxy resins. Especially in terms of flame retardancy and thermal stability, the difference is obvious. Recent studies have shown that modified phenolic resins formed by introducing DOPO into phenolic resins are more suitable for use as curing agents. There are also two reported modified phenolic resins X and XI which are also useful as curing agents for CNE resins. The product exhibited good thermal stability (>320 ° C), high Tg (159-178 ° C), high char formation rate (N2, 70 ° C, >50%) and LOI value (26-32.5). Compared with DOPO derivative III, these modified phenolic resins have similar properties, but because the modified phenolic resin has better compatibility with the polymer, the process is relatively simple and the cost is lower, so that it can be better promoted. Applications, both of which are useful as curing agents for epoxy resins in semiconductor packages and electronic laminates.
The introduction of DOPO derivatives as flame retardants and curing agents into epoxy resins improves the flame retardancy and thermal stability of epoxy resins, and more importantly, avoids the use of brominated epoxy resins in the process of use and recycling. The pollution caused has opened up a new path for the development of epoxy resin. Experts believe that the development and application of DOPO derivatives in the future will need to solve two or two problems: simplifying the process from DOPO synthesis, reducing costs, laying a solid foundation for the final reduction of DOPO derivative costs and more favorable participation in market competition; The synergistic effect of phosphorus, nitrogen and other non-halogen elements in DOP0 derivatives expands the types of DOPO derivatives and their fields of application. At present, Sichuan Oriental Insulation Materials Co., Ltd. has made great progress in the development and application of DOPO and its derivatives, and has also cooperated extensively with many research institutes such as Beijing Institute of Chemistry, Chinese Institute of Organic Chemistry, and Sichuan University. . It is believed that in the near future, DOPO and its derivatives will not only be epoxy resins, but also contribute more and more to the development of other halogen-free flame retardant materials.